| Type: | E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes) |
|---|---|
| Material: | Tungsten |
| Welding Core Type: | Carbon Structural Steel |
|
Still deciding? Get samples of US$ 10/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product |
E6013 , E6011,E6010,E7018,J422 , stainless steel welding rod E308, E309,E316 |
| Size | 2.0x300mm,2.5x300mm,3.2x350mm,3.2x400mm,4.0x400mm,4.0x450mm |
| Brand | We can customized the carton and brand. |
| Packing |
2.5kg/inner box, 8boxes/carton 5kg/ineer box, 4boxes/carton 1ton or 2 ton / pallet |
Welding Electrode AWS E6013 is a low carton steel electrode with high titanium-potassium type coating, and suitable for both AC and DC.
Welding Electrode AWS E7018 is a high-quality carbon steel electrode with iron powder and low hydrogen potassium type coating.can weld mild steel, weld high strength and low alloy steel.
Welding Electrode AWSE6011 and E6010 are special carbon steel electrodes for vertical down welding with cellulose potassium coating. It is used for butt, fillet and lap welding of thin plate structures, such as air ducts, flues, oil tanks of transformers, ship hulls, etc.
|
Welding electrode
|
|
|
Model
|
E6013 / J421
|
|
Product Name
|
welding electrode
|
|
Net weight
|
20KG / carton
|
|
Packing
|
4 boxes* 5kg per inner box
|
|
Material
|
Steel alloy
|
|
MOQ
|
26
|
|
Chemical Composition of Deposited Metal (%)
|
|||||
|
Chemical Composition
|
C
|
Mn
|
Si
|
S
|
P
|
|
Guarantee Value
|
≤0.12
|
0.3~0.6
|
≤0.35
|
≤0.035
|
≤0.040
|
|
Mechanical Properties of Deposited Metal
|
|||||
|
Test Item
|
Rm(MPa)
|
ReL(Mpa)
|
A(%)
|
KV2(J)
|
KV2(J)
|
|
Guarantee Value
|
≥420
|
≥330
|
≥17
|
-(normal temperature)
|
-(0ºC)
|
|
General Result
|
460~540
|
≥340
|
18~26
|
50~80
|
≥47
|
|
Reference Current (AC, DC)
|
|||||
|
Electrode Diameter(mm)
|
φ2.0
|
φ2.5
|
φ3.2
|
φ4.0
|
φ5.0
|
|
Welding Current (A)
|
40~70
|
50~90
|
90~130
|
130~210
|
170~230
|
|
X-ray Radiographic Inspection: Degree
|
|||||